000002193 24500 $$aSTUDY ON THE BASIC PROPERTIES OF LOW CARBON CONCRETE WITH HIGH AMOUNT OF ADMIXTURE

000002193 24630 $$n1.$$pProceedings of the First International Conference on Concrete Sustainability
000002193 260__ $$bJapan Concrete Institute, Tokyo
000002193 506__ $$arestricted
000002193 520__ $$2eng$$aThe properties of concrete with high amount of the mineral admixtures with a few carbon footprint other than cement were showed. The experiment examines the influence that mixing ratio gives to fresh property, strength property and durability of low carbon concrete. As the results, although the mixing ratio of the cement in the binder is 30% or less, the compressive strength could be achieved up to 50N/mm2 at 28 days by designing appropriate water-binder ratio. In the case of the same water-binder ratio, the drying shrinkage and freezing and thawing resistance of low carbon concrete were equivalent to the concrete which used only the ordinary portland cement.

000002193 540__ $$aText je chráněný podle autorského zákona č. 121/2000 Sb.
000002193 653__ $$aｌow carbon concrete, admixture, fresh property, strength property, durability, carbon dioxide emission

000002193 7112_ $$aFirst International Conference on Concrete Sustainability$$cTokyo (JP)$$d2013-05-27 / 2013-05-29$$gICCS13
000002193 720__ $$aKOBAYASHI, Toshimitsu$$iICHISE, Kenichi$$iMIZOBUCHI, Asako$$iCHIKAMATSU, Ruichi
000002193 8560_ $$ffischerc@itam.cas.cz
000002193 8564_ $$s932618$$uhttp://invenio.itam.cas.cz/record/2193/files/S3-5-1.pdf$$y
             Original version of the author's contribution as presented on CD, .
            
000002193 962__ $$r2053
000002193 980__ $$aPAPER