000021272 24500 $$aTHE USE OF WELDING FOR FORMING FEAL COATING ON S235

000021272 24630 $$n23.$$pEngineering Mechanics 2017
000021272 260__ $$bBrno University of Technology, Institute of Solid Mechanics, Mechatronics and Biomechanics, Brno
000021272 506__ $$arestricted
000021272 520__ $$2eng$$aImplementation of new materials into industrial practice allows to build more durable and reliable machine parts suitable to operate at high temperature and other special conditions. The paper analyzes implementation of welding method to make intermetallic surface Fe40Al5CrTiB on material grade S235JR. The process was made with tungsten inert gas (TIG) and with the use of reserved polarity direct current (DC-). Welded sample was made as: single bead, multi bead and as multilayer. After the welding process, samples were tested with geometric measurement, Vickers hardness (HV), light microscopy (LM) and scanning electron microscopy (SEM). This technology can by used to develop resistance surfaced in the power industry in the future.

000021272 540__ $$aText je chráněný podle autorského zákona č. 121/2000 Sb.
000021272 653__ $$aCoating, FeAl, Intermetallic, Imperfection, TIG.

000021272 7112_ $$aEngineering Mechanics 2017$$cSvratka, CZ$$d2017-05-15 / 2017-05-18$$gEM2017
000021272 720__ $$aCebulski, J.$$iPasek, D.$$iBęczkowski, R.
000021272 8560_ $$ffischerc@itam.cas.cz
000021272 8564_ $$s949480$$uhttps://invenio.itam.cas.cz/record/21272/files/0230.pdf$$yOriginal version of the author's contribution in proceedings, page 230, section REL.
000021272 962__ $$r21225
000021272 980__ $$aPAPER