000022898 24500 $$aFatigue life tests of thick bondline adhesively-bonded joints under constant amplitude loading conditions

000022898 24630 $$n24.$$pEngineering Mechanics 2018
000022898 260__ $$bInstitute of Theoretical and Applied Mechanics of the Cech Academy of Sciences, Prague
000022898 506__ $$arestricted
000022898 520__ $$2eng$$aThe study presents the test results of thick bondline adhesive-bonded joints in variable load conditions at loading cycle asymmetry coefficient R = 0. The study included the following samples: G1 group (without aging), G5 group (samples stored for 4 weeks in water at 20 ÂşC) and G7 group (samples stored for 1 week in water at 20 ÂşC, and sealed air-tight for 1 week in a water and moisture barrier film at 70ÂşC). Fatigue life results for G1 and G5 samples do not show significant differences for each load level indicating that the ageing conditions used for G5 samples did not affect the fatigue life. The comparison of the S-N curves for G1 and G7 samples shows significant differences indicating that the ageing conditions used for G7 samples resulted in an increase in fatigue life compared to G1 samples without ageing). Significant differences can be observed depending on the load level.

000022898 540__ $$aText je chráněný podle autorského zákona č. 121/2000 Sb.
000022898 653__ $$aadhesive joint, rail vehicle, aging of adhesive joints, fatigue life, S-N curves

000022898 7112_ $$aEngineering Mechanics 2018$$cSvratka, CZ$$d2018-05-14 / 2018-05-17$$gEM2018
000022898 720__ $$aTopoliński, T.$$iMazurkiewicz, A.$$iLigaj, B.$$iSlomion, M.
000022898 8560_ $$ffischerc@itam.cas.cz
000022898 8564_ $$s286403$$uhttps://invenio.itam.cas.cz/record/22898/files/861.pdf$$yOriginal version of the author's contribution in proceedings, page , section SOL.
000022898 962__ $$r21225
000022898 980__ $$aPAPER