000009297 24500 $$aFatigue crack growth and delamination in fiber metal laminate (glare) during loading with positive mean stress

000009297 24630 $$n18.$$pEngineering Mechanics 2012
000009297 260__ $$bInstitute of Theoretical and Applied Mechanics, AS CR, Prague
000009297 506__ $$arestricted
000009297 520__ $$2eng$$aThe aim of the paper is to present the results of a study on the damage of fiber metal laminate (GLARE) subjected to the low cycle fatigue loading with positive mean stress. The fatigue crack initiation and growth was observed on the surface of notched specimens and then the individual layers of fatigued specimens were removed by chemical etching and polishing to obtain data about cracks length and delamination shape and area. Mechanism of initiation and crack growth in this type of materials differs from homogeneous monolithic materials. The fatigue life in term of number of cycles to crack initiation depending on amplitude of local plastic deformation and local stress in the notch root was evaluated.

000009297 540__ $$aText je chráněný podle autorského zákona č. 121/2000 Sb.
000009297 653__ $$afatigue, laminate, crack initiation, crack growth, delamination

000009297 7112_ $$aEngineering Mechanics 2012$$cSvratka (CZ)$$d12/05/2014 - 15/05/2014$$gEM2012
000009297 720__ $$aChlupová, A.$$iKozák, V.
000009297 8560_ $$ffischerc@itam.cas.cz
000009297 8564_ $$s321680$$uhttps://invenio.itam.cas.cz/record/9297/files/300_Chlupova_A-FT.pdf$$yOriginal version of the author's contribution as presented on CD, paper (No. 300).
000009297 962__ $$r8924
000009297 980__ $$aPAPER