1.
|
Padevět, P.
Paper described material properties of cement pastes. Cement pastes were made from portland cement. Various water-cement ratio were used (from 0,3 to 0,5). From paste the [...]
|
2.
|
Abstrakt: The integral concepts for calculation of the generalized stress intensity factor and elastic T stress are presented. Both the integrals are based on a validity [...]
|
3.
|
Three point bending test of central notched specimen is used for determination of fracture properties of concrete, mortar and hardened cement paste. The properties – e. [...]
|
4.
|
The contribution deals with a complicated problem of fatigue damage of structure parts, which are loaded by a combination of random forces in tension-pressure and moments [...]
|
5.
|
Abdominal aortic aneurysm is usually manifested like balloon dilation of the distal aorta. This bulge is probably caused by degradation processes in an arterial wall. Sha [...]
|
6.
|
The aim of this paper is to investigate the beginnings of crack propagation from sharp V-notches. Stress distribution around the tip of a V-notch is described on the basi [...]
|
7.
|
Temperature evolution in concrete constructions due to hydration heat presents a formidable problem causing early age cracking and from the chemical point of view changin [...]
|
8.
|
Presented paper deals with computational fatigue strength prediction of high pressure level steam turbine blade pin joints. Quazi-static FE analysis of one turbine disk s [...]
|
9.
|
Selected approximation curves of mechanical-fracture parameter values − modulus of elasticity, effective fracture toughness, specific fracture energy, compressive cube [...]
|
10.
|
This paper examines the influence of reinforcement steel elemental composition and surface condition (polished and unpolished) on the corrosion rate of reinforced concret [...]
|
11.
|
Abstrakt: Relations between crack opening displacement (CTOD) and other fracture mechanics parameters are of a great importance in fracture mechanics. The basic aim of t [...]
|
12.
|
Krejčí, P.
For a complete description of two-phase flow a basic information about liquid phase formation is needed. The information is fulfilled in terms of nucleation rate and its [...]
|
13.
|
Semi-solid or mushy state processing permits a material to partially solidify before shape making operations. The understanding of material behaviour in the mushy state i [...]
|
14.
|
Presented paper deals with fracture behaviour of carbon fibre reinforced composites on the basis of Portland (PC) and alumina (HC) cement. Carbon fibres can be used for [...]
|
15.
|
The stability criteria of V-notched bodies under combination of loading modes I and II are suggested and compared in the article. Methodology of stability criterion sugge [...]
|
16.
|
Under the consideration of the bi-material notch composed of two orthotropic materials the potential direction of the crack initiated from the notch tip is determined fro [...]
|
17.
| |
18.
| |
19.
| |
20.
|
A 3D elastic-plastic FEM model with small strains was used for simulation of the deformation mechanics at the curved front of the planar fatigue crack growing in the thic [...]
|
21.
|
Corrosion of reinforcing steel in concrete is one of the most influencing factors causing the degradation of reinforced concrete structures, conducting to concrete crack [...]
|
22.
|
This article is focused on the computational solution of the material tests and their evaluations. Problem deals with torsion low-cycle fatigue tests of steel specimens. [...]
|
23.
|
Ferfecki, P.
For the purpose of efficient diagnostics of fault conditions the influence of transverse fatigue crack on dynamical behaviour of a rotor system supported by active magnet [...]
|
24.
|
Cyclic tests with the maximum force in a cycle Fmax = 5,5 kN and the cycle asymmetry ratio R = F min / F max = 0, 1 were carried out on fiat specimens of 5mm in thickness [...]
|
25.
|
This article shows: 1. Some studies of a low-cycle material fatigue caused by cyclical contact between two spheres with the same diameters. The spheres are made up from m [...]
|
26.
|
The influence of corner singularity on crack behaviour for a threedimensional structure is described in this paper. The distribution of stress singularity through the thi [...]
|
27.
|
The basic fracture properties of cement-based composite are ascertained on the basis of test evaluations of the specimens in suitable test configurations. Three-point ben [...]
|
28.
|
The calibration of the potential method DC/PD is calculated for the side-grooved CT-sample with point current inputs. The grooves are modelled by a line transition resist [...]
|
29.
|
In this paper is solved a 3D analysis of growing crack of the chevron notched three-point-bending specimen. On macroscale the specimen body is modeled as an elastic homog [...]
|
30.
|
The contribution deals with the 3D analysis of the chevron notched three point bending specimen which is used to determine the fracture toughness of brittle matrix compos [...]
|
31.
|
The paper is devoted to fatigue crack propagation in layered materials. The influence of plasticity induced crack closure on threshold values for fatigue crack propagatio [...]
|
32.
| |
33.
|
The crack growth prediction techniques in the critical area of the small transport aircraft undercarriage bracket has been describe in this paper. Stress-state was determ [...]
|
34.
|
To the interpretation of crack growth, it is substantial to estimate the plastic region geometry in front of a crack. Performed here is a study for predicting crack growt [...]
|
35.
|
Structures operating at high temperatures are damaged by creep processes. If the structure is also subjected to cyclic loading, the fatigue damage is usually significant. [...]
|
36.
|
A two-parameter fracture mechanics method is applied to small cracks near a stress concentrator. The small crack in the present contribution is considered as crack influe [...]
|
37.
|
This contribution presents a simple numerical model for crack growth under mode-I compressive fatigue loading. Residual tensile stress at the crack tip, which is responsi [...]
|
38.
| |
39.
|
The article is a contribution to numerical simulations of pitting arise phenomena on the gear teeth. The basic assumption of the presented simulations was that pitting (p [...]
|
40.
|
The fatigue crack growth rate in the Eurofer 97 steel was measured by two different methodologies. Small crack growth data were obtained using cylindrical specimens with [...]
|