1.
|
The contribution deals with a complicated problem of fatigue damage of structure parts, which are loaded by a combination of random forces in tension-pressure and moments [...]
|
2.
|
Ferfecki, P.
For the purpose of efficient diagnostics of fault conditions the influence of transverse fatigue crack on dynamical behaviour of a rotor system supported by active magnet [...]
|
3.
|
This paper presents a simulation of 3D curved crack propagation in a steam turbine blade lock. These fatigue cracks are often initiated near a blade root contact zone. Tw [...]
|
4.
|
This paper deals with a damage-plasticity model combining Mises plasticity with isotropic damage. Due to softening induced by damage growth, the governing differential eq [...]
|
5.
| |
6.
| |
7.
|
The Leonov model, where the Eyring flow model is used to represent the plastic shear rate of the deformation of a material, appears to be a proper choice for the descript [...]
|
8.
|
The probability calculation using two variants of Weibull weakest-link theory is presented in this article. The first varian assumed only one tensile stress (the first pr [...]
|
9.
|
Key green policies of Korea, such as Low Carbon Green Growth, Target Management, and Emission Trading, are first introduced. Recent efforts to systematically develop envi [...]
|
10.
|
Cracking behavior of lime mortar renders subjected to shrinkage is numerically investigated by the finite element method (FEM). The render materials selected for the stud [...]
|
11.
| |
12.
|
The calibration of the potential method DC/PD is calculated for the side-grooved CT-sample with point current inputs. The grooves are modelled by a line transition resist [...]
|
13.
|
Cyclic tests with the maximum force in a cycle Fmax = 5,5 kN and the cycle asymmetry ratio R = F min / F max = 0, 1 were carried out on fiat specimens of 5mm in thickness [...]
|
14.
|
Selected approximation curves of mechanical-fracture parameter values − modulus of elasticity, effective fracture toughness, specific fracture energy, compressive cube [...]
|
15.
|
Kafka, Vratislav
Abstrakt: Inelastic macroscopic behavior of technical as well as biological materials is strongly related to their structures. Therefore, constitutive modeling of the res [...]
|
16.
|
Abstrakt: The long-term behaviour of a crystalline rock has been modelled as a viscoplastic problem. The Perzyna type of material models, which is based on socalled overs [...]
|
17.
|
This article is focused on the computational solution of the material tests and their evaluations. Problem deals with torsion low-cycle fatigue tests of steel specimens. [...]
|
18.
|
In this paper is solved a 3D analysis of growing crack of the chevron notched three-point-bending specimen. On macroscale the specimen body is modeled as an elastic homog [...]
|
19.
|
A 3D elastic-plastic FEM model with small strains was used for simulation of the deformation mechanics at the curved front of the planar fatigue crack growing in the thic [...]
|
20.
|
The contribution deals with the 3D analysis of the chevron notched three point bending specimen which is used to determine the fracture toughness of brittle matrix compos [...]
|
21.
|
A two-parameter fracture mechanics method is applied to small cracks near a stress concentrator. The small crack in the present contribution is considered as crack influe [...]
|
22.
|
When we approach the subject of construction and rehabilitation of buildings we necessarily must think about external wall coatings as they are the elements more exposed [...]
|
23.
|
The crack growth prediction techniques in the critical area of the small transport aircraft undercarriage bracket has been describe in this paper. Stress-state was determ [...]
|
24.
|
Corrosion of reinforcing steel in concrete is one of the most influencing factors causing the degradation of reinforced concrete structures, conducting to concrete crack [...]
|
25.
|
To the interpretation of crack growth, it is substantial to estimate the plastic region geometry in front of a crack. Performed here is a study for predicting crack growt [...]
|
26.
| |
27.
|
Structures operating at high temperatures are damaged by creep processes. If the structure is also subjected to cyclic loading, the fatigue damage is usually significant. [...]
|
28.
|
This article shows: 1. Some studies of a low-cycle material fatigue caused by cyclical contact between two spheres with the same diameters. The spheres are made up from m [...]
|
29.
|
The fatigue crack growth rate in the Eurofer 97 steel was measured by two different methodologies. Small crack growth data were obtained using cylindrical specimens with [...]
|
30.
|
The article is a contribution to numerical simulations of pitting arise phenomena on the gear teeth. The basic assumption of the presented simulations was that pitting (p [...]
|
31.
|
This contribution presents a simple numerical model for crack growth under mode-I compressive fatigue loading. Residual tensile stress at the crack tip, which is responsi [...]
|