The paper deals with material models calibration from experiment tests on cylindrical bar. There are calibrated four ductile damage criteria, which seem to be generally w [...]
|
5.
|
This paper presents a simulation of 3D curved crack propagation in a steam turbine blade lock. These fatigue cracks are often initiated near a blade root contact zone. Tw [...]
|
6.
|
Seven ductile fracture criteria are applied to simulation of cold forward extrusion and their performance in prediction of chevron cracks is presented. The criteria are i [...]
|
7.
|
Procedures FITNET were developed by the European Fitness-for-service Thematic Network. One of the modules of this procedure is module fatigue of materials and constructio [...]
|
8.
|
Selected approximation curves of mechanical-fracture parameter values − modulus of elasticity, effective fracture toughness, specific fracture energy, compressive cube [...]
|
9.
|
Cichański, A.
The paper presents results of research on precision of stress concentration factor for flat bars with opposite U-shaped notches under tension. The calculations were perfo [...]
|
10.
| |
11.
|
Abstrakt: Relations between crack opening displacement (CTOD) and other fracture mechanics parameters are of a great importance in fracture mechanics. The basic aim of t [...]
|
12.
|
Structures operating at high temperatures are damaged by creep processes. If the structure is also subjected to cyclic loading, the fatigue damage is usually significant. [...]
|
13.
|
This article shows: 1. Some studies of a low-cycle material fatigue caused by cyclical contact between two spheres with the same diameters. The spheres are made up from m [...]
|
14.
|
Corrosion of reinforcing steel in concrete is one of the most influencing factors causing the degradation of reinforced concrete structures, conducting to concrete crack [...]
|
15.
|
The contribution discusses possible approach for the formulation of fracture criteria for the general stress concentrators – especially a surface crack terminating at t [...]
|
16.
|
Maekawa, Shin
Wall paintings of the Mogao Grottoes have survived for a millennium in the cool-dry cave environment in the northwestern desert of China. Visitor numbers have been steadi [...]
|
17.
| |
18.
|
The paper proposes, on built heritage reuse, a research collaboration within the University of Naples Federico II and Faculty of Architecture and Design, COMSATS, of Isla [...]
|
19.
|
Abstrakt: The presented paper deals with procedure created for quality and reliability evaluation of ductile fracture criteria group. The base for criteria verification i [...]
|
20.
|
Abstrakt: Existence of the interface between regions with different elastic properties have a pronounced influence on the behaviour of cracks The aim of the present contr [...]
|
21.
|
The paper deals with an old problem of praxis. Structures, in general, are exposed to random excitations, which generate normal and torsional stresses. While an estimatio [...]
|
22.
|
Paper is focused on comprehensive solution of probabilistic integrity assessment of pressure vessels. Engineering criteria was fully respected during solution, however fr [...]
|
23.
|
Presented paper deals with fracture behaviour of carbon fibre reinforced composites on the basis of Portland (PC) and alumina (HC) cement. Carbon fibres can be used for [...]
|
24.
|
Fracture behaviour of concrete is studied using two-phase material model. Propagation of a single macrocrack in hardened cement paste (matrix) and aggregate (particle) is [...]
|
25.
|
A 3D elastic-plastic FEM model with small strains was used for simulation of the deformation mechanics at the curved front of the planar fatigue crack growing in the thic [...]
|
26.
|
The crack growth prediction techniques in the critical area of the small transport aircraft undercarriage bracket has been describe in this paper. Stress-state was determ [...]
|
27.
|
Cyclic tests with the maximum force in a cycle Fmax = 5,5 kN and the cycle asymmetry ratio R = F min / F max = 0, 1 were carried out on fiat specimens of 5mm in thickness [...]
|
28.
|
Three point bending test of central notched specimen is used for determination of fracture properties of concrete, mortar and hardened cement paste. The properties – e. [...]
|
29.
|
In this paper is solved a 3D analysis of growing crack of the chevron notched three-point-bending specimen. On macroscale the specimen body is modeled as an elastic homog [...]
|
30.
|
Under the consideration of the bi-material notch composed of two orthotropic materials the potential direction of the crack initiated from the notch tip is determined fro [...]
|
31.
| |
32.
| |
33.
| |
34.
|
The contribution deals with the 3D analysis of the chevron notched three point bending specimen which is used to determine the fracture toughness of brittle matrix compos [...]
|
35.
|
In case of two-parameter linear fracture mechanics a study of inhomogeneity influence on behaviour of short cracks is performed. The values of stress intensity factor (KI [...]
|
36.
|
This paper is focused on fracture energy which belongs to the basic fracture-mechanical characteristics of quasi-brittle materials. This parameter is explored here from t [...]
|
37.
|
The fatigue crack growth rate in the Eurofer 97 steel was measured by two different methodologies. Small crack growth data were obtained using cylindrical specimens with [...]
|
38.
|
This contribution presents a simple numerical model for crack growth under mode-I compressive fatigue loading. Residual tensile stress at the crack tip, which is responsi [...]
|
39.
|
The stability criteria of V-notched bodies under combination of loading modes I and II are suggested and compared in the article. Methodology of stability criterion sugge [...]
|
40.
|
This paper presents the consideration on the change judgement of J integral and Q parameter as the base parameters of two-parameter elastic-plastic fracture mechanics. An [...]
|
41.
|
The article is a contribution to numerical simulations of pitting arise phenomena on the gear teeth. The basic assumption of the presented simulations was that pitting (p [...]
|
42.
|
To the interpretation of crack growth, it is substantial to estimate the plastic region geometry in front of a crack. Performed here is a study for predicting crack growt [...]
|
43.
|
The basic fracture properties of cement-based composite are ascertained on the basis of test evaluations of the specimens in suitable test configurations. Three-point ben [...]
|
44.
|
Under the assumptions of linear elastic fracture mechanics the behaviour of cracks and general singular stress concentrators is studied and compared. The stress distribu [...]
|
45.
|
The aim of this paper is to investigate the beginnings of crack propagation from sharp V-notches. Stress distribution around the tip of a V-notch is described on the basi [...]
|
46.
|
A two-parameter fracture mechanics method is applied to small cracks near a stress concentrator. The small crack in the present contribution is considered as crack influe [...]
|